Element distribution in the corrosion layer and cytotoxicity of alloy Mg-10Dy during in vitro biodegradation

The present work investigates the corrosion behaviour, the element distribution in the corrosion layer and the cytocompatibility of alloy Mg-10Dy. The corrosion experiments were performed in a cell culture medium (CCM) under cell culture conditions close to the in vivo environment. The element distribution on the surface as well as in cross-sections of the corrosion layer was investigated using scanning electron microscopy, energy-dispersive X-ray analysis, X-ray photoelectron spectroscopy and X-ray diffraction. The cytocompatibility of alloy Mg-10Dy with primary human osteoblasts was evaluated by MTT, cell adhesion and live/dead staining tests. The results show that the corrosion layer was enriched in Dy, while the P and Ca content gradually decreased from the surface to the bottom of the corrosion layer. In addition, large amounts of MgCO₃·3H₂O formed in the corrosion layer after 28 days immersion. Both extracts and the Dy-enriched corrosion layer of alloy Mg-10Dy showed no cytotoxicity to primary human osteoblasts.